Drew
Mn stringers were not uncommon in the light gauge stainless that we used, .026 to .045. The more you roll the metal the longer and wider they get. The mills could elimenate the Mn but less than .7 percent Mn caused stress cracking. I have had stress cracking cause a forearm iron on a super to break but seldom see anyone mention this problem.

bill