Thanks for the updates. I would have originally guessed the different images might have shown more welding flaws and inclusions, but they really do look good in your samples. Though they could detect a difference between the iron and steel, once welded and twisted, it does seem like the working barrel behaves like a monosteel.

Looking forward to any tensile strength comments you're able to share.