So 2-piper is it possible to color and not harden with a cyanide process and is it at a temperature low enough to not soften the metal (4140) too much? And I agree that with 4140 I would rather have a blue receiver. But some insist that case color is a must. Personally I find most cyanide colors to be too brash.