I think many folks have seen wrought iron inclusions (silicates?), but there's usually a 'grain' to it. I see lines that cross near ninety degrees to each other, might be hard to do that by forging metal without some distortion.

I'd still guess, in that particular picture, maybe those are rough filing marks that telegraphed through the finish because they weren't seen or the part was taken to some final dimension.