What I find most interesting is how deep of a case depth you can achieve at the lower temp ranges. Something some so called "experts" say can not be done. It's nice to have numbers to back up what I have always suspected and observed in the trials I have run over the years. I have also found warpage and quench cracking to be much less of a problem when staying below 1500 deg.