Kirk,
I suggest you use either water hardening or oil hardening "drill rod", available from either local or mail order industrial supply houses. A 36 is typically a "Structural steel" and may have enough carbon to harden, but I think it will be easier to use tool steel. I would harden it like a spring. This is only a suggestion.
Mike