I noted that it was mentioned that HiForce 44 had a lower "critical" temp than what the barrel ribs were originally soldered with. I would think the barrels would have been soldered with 60/40 Tin/Lead solder? That would have a 360F melting temp. My recollection of the HiForce solder I used on my project was that it melted at 475F.