Originally Posted By: keith
A couple references I looked at claim that cyanide case hardening produces a higher surface hardness than charcoal pack hardening because the cyanide process nitrides the surface as well as carburizes it....

I found that later too Keith, and apparently it's not just a carburizing process. A thing that may matter though is that the hardenabilty is increased, but not necessarily the hardness.