"What Sam mentioned, particularly around 900*, is actually not tempering, but a process that might be called spheroidizing annealing."

Craig, you are right there. Engravers are only interested in getting the metal drawn back to a level easily engraved. If too soft it will ding too easily making for a lot of minor cleanup/polishing during the project.

Sam Welch