I'd add one caviat to Toby's observation. That being, the cool down from normalization temperature would have to be controlled/slowed sufficiently to avert the air quench Chuck refers to. One method might be to immediately bury the barrels (especially the weld zone while still above normalization temperature) in sand and allow them to cool while buried. The elegant way would be to heat and cool in a temperature controlled furnace.