Glad this has worked out OK for you. A small warp that requires a small bend is not a big surprise. After all, manufactureres had Hard Fitters to deal with warps in the initial casing of the action. What you described seemed to be a very big warp and would have indicated a serious problem in the process. Case hardening of mild steel is well enough understood that there should be no big problems when done to known procedures.