Originally Posted By: Chuck H

Craig
your understanding is incorrect. Steel has a Young's modulus that is unchanged by heat treat.


Sorry Chuck, I thought that's what I was thinking. That elasticity is unchanged with hardness and both samples would permanently deform at the same point. If Young's modulus were followed, can you make the hardened sample deflect farther than the soft sample and return to true.